Diran™ 410MF07
Material Data Sheet
Diran™ 410MF07
Diran™ 410MF07 is a nylon-based thermoplastic FDM® material, mineral-fi lled 7% by weight. It demonstrates very good toughness and impact strength combined with resistance to hydrocarbon-based chemicals. Its smooth, lubricious surface quality offers low sliding resistance.
Typical applications include jigs, fixtures and other forms of general manufacturing tooling, and is particularly effective for applications needing a non-marring interface between the tool and the workpiece.
Color options:
Black
Quick Facts:
- N/A
| Phsyical Properties | Test Method | Typical Values XY | Typical Values XZ/ZX |
|---|---|---|---|
| HDT @ 66psi | ASTM D648 Method B | 90 °C (194 °F) | 90 °C (194 °F) |
| HDT @ 264 psi | ASTM D648 Method B | 70 °C (158 °F) | 70 °C (158 °F)) |
| Tg | ASTM D7426 Inflection Point | 117 °C (243 °F) | 117 °C (243 °F) |
| Mean CTE | ASTM E831 (40 °C to 140 °C) | 55 µm/[m*°C] 31 µin/[in*°F] |
113 µm/[m*°C] 63 µin/[in*°F] |
| Volume Resistance | ASTM D257 | 1.5*1015 Ω cm | 1.5*1015 Ω cm |
| Dielectric Constant | ASTM D150 1 kHz test condition | 3.58 | 3.73 |
| Dielectric Constant | ASTM D150 2 kHz test condition | 2.85 | 2.95 |
| Dissipation Factor | ASTM D150 1 kHz test condition | 0.013 | 0.014 |
| Dissipation Factor | ASTM D150 2 kHz test condition | 0.000 | 0.012 |
| Specific Gravity | ASTM D792 @ 23 °C | 1.16 | 1.16 |
| Tensiles Properties: ASTM D638 | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Yield Strength | MPa | 45 (2) | No yield) |
| psi | 6,490 (22) | No yield | |
| Elongation @ Yield | % | 4.26 (0.04) | No yield |
| Strength @ Break | MPa | 40 (3) | 30 (2) |
| psi | 5,860 (440) | 4,460 (295) | |
| Elongation @ Break | % | 12 (3) | 3.1 (1.0) |
| Modulus (Elastic) | GPa | 1.69 (0.02) | 1.46 (0.02) |
| ksi | 245 (3) | 210 (3) |
| Flexural Properties: ASTM D790, Procedure A | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Strength @ Break | MPa | No break | No break |
| psi | No break | 6,770 (325) | |
| Strength @ 5% Strain | MPa | 60 (2) | – |
| psi | 8,800 (230) | – | |
| Strain @ Break | % | No break | 3.1 (0.6) |
| Modulus | GPa | 1.85 (0.04) | 1.47 (0.04) |
| ksi | 270 (6) | 210 (10) |
| Compression Properties: ASTM D695 | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Yield Strength | MPa | 75 (5) | 160 (30) |
| psi | 10,980 (630) | 23,560 (4330) | |
| Modulus | GPa | 1.54 (0.03) | 1.45 (0.02) |
| ksi | 220 (4) | 210 (3) |
| Impact Properties: ASTM D256, ASTM D4812 | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Izod, Notched | J/m | 380 (135) | 27 (5) |
| ft*lb/in | 7 (3) | 0.5 (0.1) | |
| Izod, Unnotched | J/m | 1,415 (200) | 140 (25) |
| ft*lb/in | 25 (4) | 2.6 (0.5) |
Values in parentheses are standard deviations.
Download pfd for technical specifications.