ABS-CF10
Material Data Sheet
ABS-CF10
Stratasys ABS-CF10 combines standard ABS (acrylonitrile butadiene styrene) material with 10% chopped carbon fiber by weight. The result is a low moisture-sensitive FDM® thermoplastic 50% stiffer and 15% stronger than standard ABS 3D printing material.
Typical applications include manufacturing tools, jigs, fixtures and end effectors that benefit from the combination of increased stiffness and reduced weight.
Color options:
Black
Quick Facts:
- N/A
| Phsyical Properties | Test Method | XY | XZ/ZX |
|---|---|---|---|
| HDT @ 66psi | ASTM D648 Method B | 100°C (212°F) | 100°C (212°F) |
| HDT @ 264 psi | ASTM D648 Method B | 99°C (210°F) | 99°C (210°F) |
| Tg | ASTM D7426 Inflection Point | 104°C (219°F) | 104°C (219°F) |
| Mean CTE | ASTM E831 (-50°C to 100°C) | 19 µm/[m*°C] 11 µin/[in*°F] |
76 µm/[m*°C] 42 µin/[in*°F] |
| Volume Resistance | ASTM D257 | 4.6 x 1012 | 4.6 x 1012 |
| Specific Gravity | ASTM D257 @23 °C | 1.0972 | 1.0972 |
| 0.010 in Layer height | |||
|---|---|---|---|
| Tensiles Properties: ASTM D638 | XZ Orientation | ZX Orientation | |
| Yield Strength | MPa | No yield | 21.2 (0.48) |
| psi | No yield | 3080 (69) | |
| Elongation @ Yield | % | No yield | 1.49 (0.08) |
| Strength @ Break | MPa | 37.7 (1.38) | 21.3 (0.48) |
| psi | No yield | 3080 (69) | |
| Elongation @ Break | % | 2.70 (0.20) | 1.49 (0.09) |
| Modulus (Elastic) | GPa | 3.342 (0.12) | 1.958 (0.028) |
| ksi | 484.6 (18) | 283.9 (4.1) | |
| Flexural Properties: ASTM D790, Procedure A | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Strength @ Break | MPa | 69.0 (2.4) | 29.2 (0.86) |
| psi | 10000 (350) | 4240 (120) | |
| Strain @ Break | % | 2.45 (0.11) | 1.89 (0.08) |
| Modulus | GPa | 3.76 (0.099) | 1.75 (0.051) |
| ksi | 545 (14) | 254 (7.5) |
| Compression Properties: ASTM D695 | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Yield Strength | MPa | No yield | No yield |
| psi | No yield | No yield | |
| Peak Strength | MPa | 73.2 (4.5) | 94.8 (2.56) |
| psi | 10620 (650) | 13740 (370) | |
| Modulus | GPa | 2.129 (0.093) | 1.917 (0.063) |
| ksi | 309 (13.6) | 278 (9.2) |
| Impact Properties: ASTM D256, ASTM D4812 | XZ Orientation | ZX Orientation | |
|---|---|---|---|
| Notched | J/m | 51.4 (1.9) | 20.3 (2.8) |
| ft*lb/in | 0.962 (0.04) | 0.381 (0.05) | |
| Unnotched | J/m | 212 (25) | 47.0 (6.4) |
| ft*lb/in | 3.97 (0.47) | 0.881 (0.12) |
Values in parentheses are standard deviations.
Download pfd for technical specifications.