ABS-M30
Material Data Sheet
ABS-M30
ABS-M30 is up to 25-30 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use parts. ABS-M30 has greater tensile, impact, and flexural strength than standard ABS.
Layer bonding is significantly stronger than that of standard ABS, for a more durable part. This results in more realistic functional tests and higher quality parts for end use.
Color options:
Natural, white, black, gray, red, and blue
Quick Facts:
- 25-30% stronger than standard ABS
- Great for bonded parts
- Real end use
| Mechanical Properties | Test Method | English | Metric |
|---|---|---|---|
| Tensile Strength (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 5,200 psi | 36 MPa |
| Tensile Modulus (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 350,000psi | 2,400 MPa |
| Tensile Elongation (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 4% | 4% |
| Flexural Strength (Method 1, 0.05”/min) | ASTM D790 | 8,800 psi | 61 MPa |
| Flexural Modulus (Method 1, 0.05”/min) | ASTM D790 | 336,000 psi | 2,300 MPa |
| IZOD Impact notched (Method A, 23°C) | ASTM D256 | 2.6 ft-lb/in | 139 J/m |
| IZOD Impact, un-notched (Method A, 23°C) | ASTM D256 | 5.3 ft-lb/in | 283 J/m |
| Thermal Properties | Test Method | English | Metric |
|---|---|---|---|
| Heat Deflection (HDT) @ 66 psi, 0.125” unannealed | ASTM D648 | 204° F | 96° C |
| Heat Deflection (HDT) @264 psi, 0.125” unannealed | ASTM D648 | 180° F | 82° C |
| Vicat Softening Temperature (Rate B/50) | ASTM D1525 | 210° F | 99° C |
| Glass Transition (Tg) | DSC (SSYS) | 226° F | 108° C |
| Coefficient of Thermal Expansion (flow) | ASTM E831 | 4.9E-05 in/in/°F | 8.82 E-05 mm/mm/°C |
| Coefficient of Thermal Expansion (xflow) | ASTM 831 | 4.7E-05 in/in/°F | 8.46E05 mm/mm/°C |
| Melt Point | – – – – – – – | Not Applicable | Not Applicable |
| Electrical Properties | Test Method | Value Range |
|---|---|---|
| Volume Resistivity | ASTM D257 | 4.0x10e14 – 5.0x10e13 ohms |
| Dielectric Constant | ASTM D150-98 | 2.9 -2.7 |
| Dissipation Factor | ASTM D150-98 | .0052 – .0049 |
| Dielectric Strength | ASTM D149-09, Method A | 370 -71 V/mil |
| Other | Test Method | Value |
|---|---|---|
| Specific Gravity | ASTM D792 | 1.04 |
| Flame Classification | UL94 | HB (0.09”, 2.50 mm) |
| Rockwell Hardness | ASTM D785 | 109.5 |
| UL File Number | – – – – – – – – – | E345258 |