ABS-M30i™
Material Data Sheet
ABS-M30i™
ABS-M30i™ is a high strength material well suited for the food packaging industries. Parts manufactured with ABS M30i material are biocompatible (ISO 10993 USP Class VI) and can be gamma or EtO sterilized.
ABS-M30i™ gives you biocompatible parts with excellent mechanical properties that are well suited for conceptual modeling, functional prototyping, manufacturing tools and end-use-parts.
Color options:
Ivory
Quick Facts:
- Biocompatible
- Food industry compliant
- Excellent mechanical properties
| English | Metric | ||||
|---|---|---|---|---|---|
| Mechanical Properties | Test Method | XZ Axis | ZX Axis | XZ Axis | ZX Axis |
| Tensile Strength, Yield (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 4,550 psi | 3,750 psi | 31 MPa | 26 MPa |
| Tensile Strength, Ultimate (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 4,650 psi | 4,050 psi | 32 MPa | 28 MPa |
| Tensile Modulus (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 320,000 psi | 310,000 psi | 2,230 MPa | 2,180 MPa |
| Tensile Elongation at Break (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 7% | 2% | 7% | 2% |
| Tensile Elongation at Yield (Type 1, 0.125”, 0.2”/min) | ASTM D638 | 2% | 1% | 2% | 1% |
| Flexural Strength (Method 1, 0.05”/min) | ASTM D790 | 8,700 psi | 7,000 psi | 60 MPa | 48MPa |
| Flexural Modulus (Method 1, 0.05”/min) | ASTM D790 | 300,000 psi | 250,000 psi | 2,060 MPa | 1,760 MPa |
| Flexural Strain at Break (Method 1 0.05”/min) | ASTM D790 | 4% | 3.5% | 4% | 3.5% |
| Mechanical Properties | Test Method | English | Metric |
|---|---|---|---|
| IZOD Impact notched (Method A, 23°C) | ASTM D256 | 2.4 ft-lb/in | 128 J/m |
| IZOD Impact, un-notched (Method A, 23°C) | ASTM D256 | 5.6 ft-lb/in | 300 J/m |
| Thermal Properties | Test Method | English | Metric |
|---|---|---|---|
| Heat Deflection (HDT) @ 66 psi, 0.125” unannealed | ASTM D648 | 204° F | 96° C |
| Heat Deflection (HDT) @ 264 psi, 0.125” unannealed | ASTM D648 | 180° F | 82° C |
| Vicat Softening Temperature (Rate B/50) | ASTM D1525 | 210° F | 99° C |
| Glass Transition (Tg) | DSC (SSYS) | 226° F | 108° C |
| Coefficient of Thermal Expansion (flow) | ASTM E831 | 4.90-05in/in/°F | 8.82-05mm/mm/°C |
| Coefficient of Thermal Expansion (xflow) | ASTM E831 | 4.70-05in/in/°F | 8.46-05mm/mm/°C |
| Melting Point | – – – – – – – | Not Applicable | Not Applicable |
| Electrical Properties | Test Method | Orientation | Value Range |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | XZ Axis | 4.0-15 – 3.3-16 ohm-cm |
| Dielectric Constant | ASTM D150-98 | XZ Axis | 2.6 – 2.86 |
| Dissipation Factor | ASTM D150-98 | XZ Axis | 0.0048 – 0.0054 |
| Dielectric Strength | ASTM D149-09, Method A | XZ Axis | 100 V/mil |
| Dielectric Strength | ASTM D149-09 Method A | ZX Axis | 360 V/mil |
| Other | Test Method | Value |
|---|---|---|
| Specifid Gravity | ASTM D792 | 1.04 |
| Flame Classification | UL94 | HB (0.09”, 2.50 mm) |
| Rockwell Hardness | ASTM D785 | 109.5 |
Download pfd for technical specifications.